1.2311德国模具钢,1.2311钢板
![](http://www.otaidg.com/d/file/20190613/71a460577eb2740c2ffe5210501681ed.jpg)
![](http://www.otaidg.com/d/file/20190613/8cbc4033c950a89d7111e24bae6ebb5e.jpg)
![](http://www.otaidg.com/d/file/20190613/0848f93137defd5550563d1ec62e37f6.jpg)
![](http://www.otaidg.com/d/file/20190613/c0c571edf96e6a412ed42c056434b063.jpg)
![](http://www.otaidg.com/d/file/20190613/8f1a763c21a7ce34911cabb995318869.jpg)
![](http://www.otaidg.com/d/file/20190613/de118f04d1047560ed2a7d42a9324af8.jpg)
![](http://www.otaidg.com/d/file/20190613/3a1e7391edb533dd4d12568cdaf0728f.jpg)
![](http://www.otaidg.com/d/file/20190613/66588b96c6d2c3f7605e92f1fed01a66.jpg)
![](http://www.otaidg.com/d/file/20190613/92650f788e6acb056879ae72e8292fa4.jpg)
1.2311钢,德国模具钢,该钢经“超纯净”工序生产,预硬化,呈现高度的微观纯净及优良的均质结构,优良的抛光性及光蚀刻花性。经热处理后,加工及抛光性能良好,可进行氮化处理,适于镀铬等表面处理,材质硬度均匀(至400mm厚),良好的韧性,良好的机械加工性能。金组织为马氏体及贝氏体组织。
状态及硬度:
调质预硬态,硬度285~325HBS.
典型化学成分:
C 0.37~0.42、Cr 1.80~2.10、Mn 1.40~1.60、Si≤0.40、Mo 0.15~0.25、S≤00.005、Ni 0.40
热加工规范:
始锻温度1050℃,终锻温度850℃,随炉缓冷。
热处理方法:
加硬处理:
为提高模具寿命达到80万模次以上,可对预硬钢实施淬火加低温回火的加硬方式来实现。淬火时先在500-600℃预热2-4小时,然后在850-880℃保温一定时间(至少2小时),放入油中冷却至50-100℃出油空冷,淬火后硬度可达50-52HRC,为防止开裂应立即进行200℃低温回火处理,回火后,硬度可保持48HRC以上
氮化处理
氮化处理可得到高硬度表层组织,氮化后的表层硬度达到650-700HV
(57-60HRC)模具寿命可达到100万次以上,氮化层具有组织致密,光滑特点,模具的脱模性及抗湿空气及碱液腐蚀性能提高。
软化退火规范:
退火温度710~740℃,炉中缓冷,硬度≤235HB。
淬火回火规范:
淬火温度840~870℃,油冷却或180~220℃盐浴,淬火后硬度51HRC,1730MPa.
回火温度100℃/200℃/300℃/400℃/500℃/600℃/700℃,硬度51HRC/50HRC/48HRC/46HRC/42HRC/36HRC/28HRC.
典型应用举例:
①用于锌、铝、镁及其合金压铸模
②热压模、各种热锻模
③金属挤压模模架
对应各国牌号:
对应国产牌号:P20 对应日本牌号:PDS-3
对应美国牌号:P20 对应瑞典牌号:618
![](http://www.otaidg.com/skin/aotai/otyx/1.jpg)
![](http://www.otaidg.com/skin/aotai/otyx/2.png)
![](http://www.otaidg.com/skin/aotai/otyx/3.png)
![](http://www.otaidg.com/skin/aotai/otyx/4.jpg)
![](http://www.otaidg.com/skin/aotai/otyx/5.jpg)
![](http://www.otaidg.com/skin/aotai/otyx/6.jpg)
上一个: SP2738mod.HH
下一个:1.2083模具钢材